Herein, a biocomposite of crosslinked chitosan polyethylene glycol diglycidyl ether (CS-PEDGE), montmorillonite (MMT), and foodgrade algae (FGA) was successfully prepared by a hydrothermal technique. The resulting absorbent (CS-PEDGE/FGA/MMT) was assessed for its adsorption property with methyl violet 2B (MV 2B) a toxic cationic dye. The physicochemical properties of CS-EDGE/ FGA/MMT were assessed via various analytical techniques, including BET, Elemental analysis, pHpzc, and spectroscopy (FTIR, XRD, SEM-EDX). The influence of three adsorption variables, namely adsorbent dose (A: 0.02–0.1 g/100 mL), solution pH (B: 4–10), and contact time (C: 10–420 min) on the rate of MV 2B dye removal was examined using the Box-Behnken design (RSM-

A new adsorbent was developed by integrating algae biomass (AG) into a chitosan (CN) matrix, followed by structural enhancement via crosslinking with pyromellitic dianhydride (PMDA) through a hydrothermal synthesis approach. This process resulted in the formation of a robust AG@CN-PMDA composite with improved physicochemical characteristics suitable for advanced adsorption applications. The AG@CN-PMDA composite was evaluated for its efficiency in removal of the cationic dye methyl violet 2B (MV 2B) from aqueous solution. The adsorption process was refined through the Box-Behnken design (RSM-BBD), evaluating three essential parameters: adsorbent dosage (A: 0.02–0.1 g/100 mL), pH (B: 4–10), and time (C: 5–20 min). The ideal conditions f

The cost-effective carbon cross-linked Y zeolite nanocrystals composite (NYC) was prepared using an eco-friendly substrate prepared from bio-waste and organic adhesive at intermediate conditions. The green synthesis method dependent in this study assures using chemically harmless compounds to ensure homogeneous distribution of zeolite over porous carbon. The greenly prepared cross-linked composite was extensively characterized using Fourier transform infrared, nitrogen adsorption/desorption, Field emission scanning electron microscope, Dispersive analysis by X-ray, Thermogravimetric analysis, and X-ray diffraction. NYC had a surface area of 176.44 m2/g, and a pore volume of 0.0573 cm3/g. NYC had a multi-function nature, sustained at a long-

Herein, date palm (Phoenix dactylifera) bunch (DPB) waste was transformed into activated carbon (DPAC) adsorbent by using microwaveinduced ZnCl2 activation for 15 min at a power of 600 W. Several analytical methods were used to explain the physicochemical parameters of DPBAC including XRD, pHpzc, BET, SEM–EDX, and FTIR. Afterwards, the adsorptive performance of DPBAC was thoroughly investigated for the removal of two structurally different organic dyes namely methyl violet (MV) and fuchsin basic (FB). The key adsorption parameters, including the dose of DPBAC (A: 0.02–0.06 g), the solution pH (B: 4–10), and the contact time (C: 2–20 min) were statistically optimized using the Box-Behnken design with response surface methodology (RSM

Wastewater discharge containing organic dyes may pose a hazard to the environment, which necessitates that dye removal must occur prior to wastewater release into water bodies. Herein, copper oxide nanoparticles (CuO NPs) were prepared by a green precipitation method to enable decolorization of a cationic dye (methyl violet; MV) from aqueous media. Complementary tools were employed to characterize the CuO NPs adsorbent: spectroscopy (FTIR and UV-VIS), microscopy (FESEM and TEM), XRD, BET surface area analysis, and point of zero charge (pHPZC) via potentiometry. The FTIR bands at 722, 663, 569, and 465 cm−1 correspond to the vibrational modes of CuO NPs, along with the optical absorbance band at 275 nm that supports the formation of Cu

Wastewater discharge containing organic dyes may pose a hazard to the environment, which necessitates that dye removal must occur prior to wastewater release into water bodies. Herein, copper oxide nanoparticles (CuO NPs) were prepared by a green precipitation method to enable decolorization of a cationic dye (methyl violet; MV) from aqueous media. Complementary tools were employed to characterize the CuO NPs adsorbent: spectroscopy (FTIR and UV-VIS), microscopy (FESEM and TEM), XRD, BET surface area analysis, and point of zero charge (pHPZC) via potentiometry. The FTIR bands at 722, 663, 569, and 465 cm1 correspond to the vibrational modes of CuO NPs, along with the optical absorbance band at 275 nm that supports the formation of CuO NPs.