In this research, the use of natural materials like wool and cannabis as intermediate reinforcement for prosthetic limbs due to their comfort, affordability, and local availability was discussed. As part of this study on below-the-knee (BK) prosthetic sockets, two sets of samples were made using a vacuum method. These sets were made of natural fiber-reinforced polymer composites with lamination 80:20: group (Y) had 4 perlon, 1 wool 4 perlon, and group (G) had 4 perlon, 1 cannabis 4 perlon. The two groups were compared with a socket made of polypropylene. Tensile testing was used to determine the mechanical characteristics of the socket materials. The Y group has a yield stress of 17 MPs, an ultimate strength of 18.75 MPa, and an elastic

Most researchers concentrate their studies on the design, stress and pressure distributions of the prosthetic socket. A little attention is considered for the stiffness of the various materials of the prosthetic sockets. Prosthetic laminated sockets in Iraq are costly to be manufactured while polypropylene socket is relatively cheap in comparing with the laminates.

Experimental study is conducted to compare the stiffness of five prosthetic sockets made of different materials. Compression, three point flexural and tensile tests are implemented by the Testometric machine. The laminate sockets give better results in compression than polypropylene. Polypropylene gives good results in bending compared with the laminate sockets. When t

Previous experimental studies have suggested that hot mixed asphalt (HMA) concrete using hydrated lime (HL) to partially replace the conventional limestone dust filler at 2.5% by the total weight of all aggregates showed an optimum improvement on several key mechanical properties, fatigue life span and moisture susceptibility. However, so far, the knowledge of the thermal response of the modified asphalt concrete and thermal influence on the durability of the pavement constructed are still relatively limited but important to inform pavement design. This paper, at first, reports an experimental study of the tensile fatigue life of HMA concrete mixes designed for wearing layer application. Tests were conducted under three different temperatur

In this research an analysis for improving the fatigue behavior (safety factor of fatigue) of non- articular prosthetic foot (SACH) in the region (Bolt Adapter).The laser peening was carried to the fatigue specimens to improving the fatigue properties of bolt’s material. The tests of mechanical properties and fatigue behavior were carried for material that the bolt manufacture from it, a region where the failure occur and inserted of these properties to the program of engineering analysis (Ansys) to calculate the safety factor of fatigue. The results showed that the safety factor after hardening by laser is increased by 42.8%.

The design of components subjected to contact stress as local compressive stress is important in engineering application especially in ball and socket Joining.  Two kinds of contact stress are introduced in the ball and socket joint, the first is from normal contact while the other is from sliding contact. Although joining two long links (drive shaft in steering cars) will cause the effect of flexural and tensional buckling stress in hollow columns through the ball and socket ends on the failure condition of the joining mechanism. In this paper the consideration of the combined effect of buckling Load and contact stress on the ball and socket joints have been taken, epically on the stress distribution in the contact area. Different

  This study included prepared samples of epoxy reinforced by the novolac , aluminum , glass powder and epoxy reinforced by aluminum , glass powder and epoxy alone .They are used as reinforced materials of volum fraction amounting 40% .  The mechanical properties inclouded ( tensile , compressive and wear) where the wear test inclouded different applied loads (5,10,15) . From the results showed the epoxy reinforced by aluminum and glass powder has higher compressive strength (56.91) Mpa and higher tensile strength (132.2) Mpa .But the epoxy alone has higher wear rate and the epoxy reinforced by aluminum and glass powder which have higher elasticity of modulus from the tensile test (315.7) Mpa

Prosthetic hands are compensatory devices for the hand amputees as a result of injury, various accidents or birth deformities, types of prosthetic hand vary depending on the mechanism they operate and how they perform. There are common types in use that are characterized by their complex mechanisms, which are difficult for the amputee to use or exclude use because of their high cost, therefore the aim of this research is to design an artificial hand that is suitable in terms of simplicity of use and low cost and similar to a natural hand with regard to dimensions and shape that operated in the mechanism of links. This research involves Stress and strain analysis of the prosthetic hand and its fingers that modelled from (Petg CR)

Mechanical Engineering Department/ University of Technology- Baghdad.

Confinement layer is considered as the most important parameter during the laser shock peening (LSP) treatment.  In this paper, its effect on the surface treatment effectivity of composite materials was investigated. The composite used in this research was fabricated using hand lay-up as a manufacturing process. The matrix material was built from unsaturated polyester resin and reinforced with 2.5% volume fraction of micro particles of aluminum powder. Fatigue test was conducted at room temperature with constant amplitude stress and a stress ratio of R =-1, before and after LSP treatment. LSP was applied with and without confinement layer at the same level

In this research, experimental and numerical studies were carried out to investigate the performance of encased glass-fiber-reinforced polymer (GFRP) beams under fire. The test specimens were divided into two peer groups to be tested under the effect of ambient and elevated temperatures. The first group was statically tested to investigate the monotonic behavior of the specimens. The second group was exposed to fire loading first and then statically tested to explore the residual behavior of the burned specimens. Adding shear connectors and web stiffeners to the GFRP beam was the main parameter in this investigation. Moreover, service loads were applied to the tested beams during the fire. Utilizing shear connectors, web stiffeners,