Prepared Electrical Resistivity Been Pure B TiO a 3 Impurity
...Show More Authors

   3 BaTiO was prepared by mixing the components of 3 BaCO and 2 TiO by ratio [1:1] ØŒ This paper is devoted to study the effect of radition on the electrical properties of 3 BaTiO . Some of prepared samples were exposed to fast neutrons   SMeV and   MeV14 . In addition ØŒ Some samples were exposed to gamma – ray with dosage   Rad81.5 10 ï‚´ . The results showed that the exposition of some samples to fast neutrons    SMeV and   MeV14 lead to increase the electrical resistivity with the study of the effect of the addition of impurity on electrical resistivity . The addition of two compounds   2 3Yb O and   2 3Sm O lead to decrease of electrical resistivity at a concentration of   0.2 % mol for both compounds ØŒ while the increase of concentration at   0.5 % mol lead to increase electrical resistivity again .    

View Publication Preview PDF
Quick Preview PDF
Publication Date
Tue Jan 08 2019
Journal Name
Iraqi Journal Of Physics
D.C electrical conductivity of prepared pure and doped polyaniline salt
...Show More Authors

Pure Polyaniline salt, and protonation PANI by H2SO4 were synthesized by electro-chemical oxidative polymerization of aniline with acidity of H2SO4. The solution was prepared in reaction temperature equal 291 K and the acidity of aqueous solution was 1 molarities. The prepared polyaniline was characterized by FT-IR, the result indicate that the intensity is increase with increasing of applied voltage. The dc conductivity has been measured for bulk polyaniline pure and doped in the form of compressed pellet with evaporated Ohmic Al electrodes in temperature range (303-423) K. The Eav energy of the thermal rate process of the electrical conductivity was determined. The results indicate that the dc conductivity of doped samples are two or t

... Show More
View Publication Preview PDF
Crossref (2)
Crossref
Publication Date
Sun Feb 03 2019
Journal Name
Iraqi Journal Of Physics
Electrical properties of pure NiO and NiO:Au thin films prepared by using pulsed laser deposition
...Show More Authors

The electrical properties of pure NiO and NiO:Au Films which are
deposited on glass substrate with various dopant concentrations
(1wt.%, 2wt%, 3wt.% and 4wt.%) at room temperature 450 Co
annealing temperature will be presented. The results of the hall effect
showed that all the films were p-type. The Hall mobility decreases
while both carrier concentration and conductivity increases with the
increasing of annealing temperatures and doping percentage, Thus,
indicating the behavior of semiconductor, and also the D.C
conductivity from which the activation energy decrease with the
doping concentration increase and transport mechanism of the charge
carriers can be estimated.

View Publication Preview PDF
Crossref (1)
Crossref
Publication Date
Mon Aug 01 2016
Journal Name
Indian Journal Of Natural Sciences
Effect of Gamma Radiation on the A.C Electrical and Dielectric Properties of Prepared Pure and Doped Polyaniline Salt
...Show More Authors

Purepolyaniline and doped with hydrochloric acid was prepared in different molarities at room temperature. The a.c electrical properties were stadied.AC conductivityσac (ω), is found to vary as ωS in the frequency range (100Hz-10MH), S< 1and decreases indicating a dominate hopping process. Thedielectric constant ε1and dielectric loss ε2 have been determined for bulk polyaniline. ε1 decrease with the increase frequency. Electrical conductivity measurements increase with the increases both of the amount of HCl and the dose of radiation. The dielectric investigations show decrease with dose radiation.

Preview PDF
Publication Date
Sun Mar 01 2020
Journal Name
Iraqi Journal Of Physics
The DC electrical Conductivity of prepared pure polypyrrole and polypyrrole /graphene (PPY/GN) nanocomposite by in-situ polymerization
...Show More Authors

Abstract

 In this work, pure Polypyrrole (PPy) and Polypyrrole (PPy)/Graphene (GN) was synthesized by in-situ polymerization in different weight percentages (0.1, 0.3, 0.5, 1, 3 and 5 wt.% (g)) of GN nano particles using chemical oxidation method at room temperature. The FTIR, SEM and electrical properties were studies for the nano composites. The result show that when concentration of GN Nano particle increase, the electrical conductivity increased and the graphene sheets were merging to form a continuous area of the GN through the polypyrrole base material. The FTIR spectra shows that the characteristics absorption peaks of polypyrrole that is, 1546.80, 1463.87 and 3400.27 cm-1(stretching vibration in the pyrrol

... Show More
View Publication Preview PDF
Crossref (2)
Crossref
Publication Date
Sun Jul 11 2021
Journal Name
Sustainable Civil Infrastructures
Field Soil Electrical Resistivity Measurements of Some Soil of Iraq
...Show More Authors

View Publication
Scopus (2)
Crossref (1)
Scopus Crossref
Publication Date
Mon Jan 01 2018
Journal Name
24th European Meeting Of Environmental And Engineering Geophysics
Electrical Resistivity Tomography of Celtic Burial Mounds in Nonnweiler (Germany)
...Show More Authors

View Publication
Scopus Crossref
Publication Date
Thu May 17 2018
Journal Name
Archaeological Prospection
Very‐high‐resolution electrical resistivity imaging of buried foundations of a Roman villa near Nonnweiler, Germany
...Show More Authors
Abstract<p>Electrical resistivity tomography (ERT) methods have been increasingly used in various shallow depth archaeological prospections in the last few decades. These non‐invasive techniques can save time, costs, and efforts in archaeological prospection and yield detailed images of subsurface anomalies. We present the results of quasi‐three‐dimensional (3D) ERT measurements in an area of a presumed Roman construction, using a dense electrode network of parallel and orthogonal profiles in dipole–dipole configuration. A roll‐along technique has been utilized to cover a large part of the archaeological site with a 25 cm electrode and profile spacing, respectively. We have designed a new field proce</p> ... Show More
View Publication
Scopus (18)
Crossref (11)
Scopus Clarivate Crossref
Publication Date
Thu Oct 01 2020
Journal Name
Iraqi Journal Of Applied Physics
Spectral and Electrical Characteristics of Nanostructured NiO/TiO 2 Heterojunction Fabricated by DC Reactive Magnetron Sputtering
...Show More Authors

In this work, p-n junctions were fabricated from highly-pure nanostructured NiO and TiO2 thin films deposited on glass substrates by dc reactive magnetron sputtering technique. The structural characterization showed that the prepared multilayer NiO/TiO2 thin film structures were highly pure as no traces for other compounds than NiO and TiO2 were observed. It was found that the absorption of NiO-on-TiO2 structure is higher than that of the TiO2-on-NiO. Also, the NiO/TiO2 heterojunctions exhibit typical electrical characteristics, higher ideality factor and better spectral responsivity when compared to those fabricated from the same materials by the same technique and with larger particle size and lower structural purity.

View Publication Preview PDF
Publication Date
Mon Mar 08 2021
Journal Name
Baghdad Science Journal
A study the electrical properties of a Se:2.5%as thin films prepared by thermal cvaporation
...Show More Authors

thin films of se:2.5% as were deposited on a glass substates by thermal coevaporation techniqi=ue under high vacuum at different thikness

View Publication Preview PDF
Crossref
Publication Date
Thu Oct 01 2009
Journal Name
Iraqi Journal Of Physics
The Structural and Optical Properties of Hydrogenated and Nitrogenated a-Si0.1Ge0.9 and a-Si0.1Ge0.9:3% B Thin Films
...Show More Authors

It is shown that pure and 3% boron doped a-Si0.1Ge0.9:H and a-Si0.1Ge0.9:N thin films
could be prepared by flash evaporation processes. The hydrogenation and nitrogenation
are very successful in situ after depositing the films. The FT-IR analysis gave all the
known absorbing bonds of hydrogen and nitrogen with Si and Ge.
Our data showed a considerable effect of annealing temperature on the structural and
optical properties of the prepared films. The optical energy gap (Eopt.) of a-Si0.1Ge0.9
samples showed to have significant increase with annealing temperature (Ta) also the
refractive index and the real part of dielectric constant increases with Ta, however the
extinction coefficient and imaginary part of dielect

... Show More
View Publication Preview PDF