The compressive residual stresses generated by shot peening, is increased in a direct proportional way with shot peening time (SPT). For each metal, there is an optimum shot peening time (O.S.T) which gives the optimum fatigue life. This paper experimentally studied to optimize shot peening time of aluminium alloy 6061-T651 as well as using of and analysis of variance (ANOVA).

Two types of fatigue test specimens’ configuration were used, one without notch (smooth) and the other with a notch radius (1,25mm), each type was shot peened at different time. The (O.S.T) was experimentally estimated  to be 8 minutes reaching the surface stresses at maximum peak of -184.94 MPa.

A response surface methodology (RSM) is presen

Background: Polymers are very rarely used in their form. These modifications are carried out in order to improve the properties of polymers.Recently silver have been used successfully as antimicrobial (medical and dental) biomaterials that can prevent caries and infection of implants Purposes: The aim of the present in vitro study is to evaluate the effect of addition of silver nitrate to acrylic resin in different concentrationsthrough several tests part of these are: The effect of this additive on impact strength, transverse strength, and tensile strength of AgNO3 – loaded resin, and to assess any effect of addition of silver nitrate on coloration of acrylic resin. Materials and methods: Different concentrations of silver nitrate

         The varied thermal conductivity (insulation) of silica aerogel with heating for different pH has been investigated, it has been depended on ambient pressure drying method in the preparing silica aerogel samples, also six different pH of samples (1, 2, 3, 7, 8 and 9) were treated under five degree of heating with (50,100,150,200 and 250) ᴼC. This technique is important to test the carry-outs hydrophobic silica to temperature without high-quality material changes in the basic characteristics. The hot-wire technique is used in this work to examine the thermal conductivity, Fourier Transform Infrared Spectroscopy (FTIR) depended to characterize the bonds and their artificial by heating. Resu

New N2O2 donor kind Schiff basehas been destined and structured by reaction Ampyrone with O-hydroxyacetophenone and Anthranilic acid. The metal complexes of the Schiff base with Mn(II), Hg(II), Ni(II), Cu(II), and Co(II) metal ions were designed and characterized by magnetic susceptibility, elemental analyses, molar conduction, IR, and 1H NMR,UV-Vis spectral metrics.The UV-Vis. and magnetic susceptibility data of the complexes suggest a square-planar, tetrahedraland octahedral geometries around the central metal ions. All elaborations were accomplished after determination the optimum molar concentration and pH which followed law of Lambert-Beer's in the researches pH scopes. The composition of these complexes were conclude dapprobating to t

Objective: The aim of this study is to detect the effect of continuous exposure to Sodium Nitrite on 8-oxoguanine
DNA glycosylase (OGG1) gene which responsible on DNA repairs. DNA repair play a major role in maintaining
genomic stability when DNA exposure to damage. Genomic stability is very important for keeping body cells
healthy and to prevent many types of tumor development. Many genes are responsible for this job; one of them is
OGG1 gene.
Methodology: In current study two groups of mice were chronically exposed to sodium nitrite for six months and
eighteen months while third group was used as a control. Then sizes of OGG1 were estimated.
Results: The results exhibited in the unexposed (control) mice had two dif

Field experiment was conducted to test the effect of saline water 2 and7 dSm-1 potassium fertilizer rate 150,300 and 450 kg/donum on nitrogen fixation in Pisum sativum L. nodules. The experiment included anatomy study .Results water salinity ( 2,7 dSm-1) as a main plot and fertilizer rates as a sub plot. Results indicated that irrigation with saline water 7 dSm-¹ caused a significant decrease in N contents especially in the lower parts of the plants. The percentage of the N decreased in lower leaves to (0.01%) under 7dSm-¹ and 300 kg/donum fertilizer; however the percentage increased in the upper leaves to (2.80%) under with 2dSm-¹of irrigation water and 300 kg/ donum fertilizer rate. Fresh weight decreased to 6.26g under 7 dSm

This Study is conducted to evaluate effects of (leaves, fruits) powder and (oil, alcohol) extract of Coriander (Coriandrum sativum) plant on some biological and physiological aspects of House fly, Musca domestica at laboratory conditions. Result show that these preparations caused biological effects represented in high dead percentage in second instar, fed on different concentrations of food treated with them reached to 27.6, 55.3 at concentration 20% of leaf and fruit powder respectively and 67.3, 77.2% at 10% of oil and alcohol extract of fruit, respectively. Furthermore, study also show reduction in pupation and adults emergence percentage. However, leafs powder had slighter effect than powder and extract of fruit of tested plant. The st

Aim: surface modification of titanium using fiber laser 1064 nm to enhance the bond strength to resin cement. Material and Methods: thirty titanium discs of 0.6 cm x 0.3 cm (diameter and thickness respectively) were categorized after preparation into three groups (n=10) as follows: control group with no surface treatment and two test groups were treated with fiber laser after estimation the appropriate parameters in the pilot study which are 81 ns pulse duration, 30,000 Hz frequency, 50 µm spot size and 10,000 mm/s scanning speed and different average power values (10 W and 20 W) depending on the tested group. Titanium discs surface characterization was performed by scanning electron microscope (SEM), a

Abstract New derivatives of 1,2,4- triazole , 1,2,4-triazole -3-one and 1,2,4-triazole-3-thione were obtained through this research. Acid hydrazide derivative was present from reaction of poly acryloyl chloride with hydrazine hydrate in presence of DMF as a solvent then reacted with benzonitrile and its derivatives to give 1,2,4-triazole derivatives. After that reaction of poly acryloyl chloride with semicarbazide and semithiocarbazide to form semicarbazone and semithiocarbazone derivatives respectively. Finally, closing of semicarbazone and semithiocarbazone derivatives with 2% NaOH gave 1,2,4-triazole -3-one and 1,2,4-triazole-4-thione derivatives respectively. These new synthesized products have been characterized by infrared, 1 H-n