In this paper, mixed spinel Co_0.4Zn_0.6Fe₂O₄ ferrite was synthesized by microwave-assisted combustion method. Photocatalytic activity of the as-synthesized sample was investigated against methylene blue dye at room temperature at different exposure times (60-360 min.) under visible light. Phase impurity and surface morphology which are investigated with XRD analysis and field emission- scanning electron microscopy, indicate that a cubic spinel unit cell structure with a crystilite size and lattice constant are 22.5048nm and 8.37Å, respectively. The saturation magnetization exhibited directly from the hysteresis loop is (70.20emu/g). Optical properties for the investigated ferrite

Abstract

      The target derivative are gentamicin linked with L-Val- L-Ala by an ester linkage. These were synthesized by esterification method, which included the reaction of -OH hydroxyl group on (carbon No.5) of gentamicin with the acid chloride of the corresponding dipeptide, The preparation of new derivative of gentamicin involved protected the primary & secondary amine groups of Gentamicin, by Ethylchloroformate (ECF) to give N-carbomethoxy Gentamicin which was used for further chemical synthesis involving the free hydroxyl groups.

Then prepared dipeptide (L-Val- L-Ala) by conventional solution method in present DCC & HoBt then reacted with thionyl

ZnxNi1-x-yCuyFe2O4 spinel ferrite were prepared using solid state reaction method with (y=0.1, x=0.2, 0.3, 0.4, 0.5, 0.6 ) . X-ray diffraction with diffractometer CuKα analysis have been carried out and studied showing single phase spinel cubic with space group FD͞ 3m for all prepared samples . Lattice parameters and crystallite grain size and x-ray density(ρx-ray) bulk density and porosity ratio's were calculated and showed good agreement with the international data reported in the scientific research's.

Ferrite with general formula Ni1-x Cox Fe2O4(where x=0.0.1,0.3,0.5,0.7, and 0.9), were prepared by standard ceramic technique. The main cubic spinel structure phase for all samples was confirmed by x-ray diffraction patterns. The lattice parameter results were (8.256-8.299 ^°A). Generally, x -ray density increased with the addition of Cobalt and showed value between (5.452-5.538gm/cm³). Atomic Force Microscopy (AFM) showed that the average grain size and surface roughness was decreasing with the increasing cobalt concentration. Scanning Electron Microscopy images show that grains had an irregular distribution and irregular shape. The A.C conductivity was found to increase with the frequency and the addition of Cobal

     We report  the influence of different glycine-to-nitrate ratios on the physical and magnetic properties for synthesized zinc-ferrite by  microwave-assisted combustion route. Phase impurity and surface morphology investigated with XRD analysis and field emission- scanning electron microscopy, indicated that  spinel structure  were  formed.Average particles size increased  with the decrease of glycine to nitrate ratio. Magnetic measurement  results indicated that  high values of saturation magnetization  were produced with low  glycine/nitrate ratio. Optical properties of  the investigated ferrites exhibited photo absorption from UV to visible region with 

New complexes of M(II) with mixed ligand of 5-Chlorosalicylic acid (CSA) C7H5ClO3 as primary ligand and L- Valine (L-Val) C5H11NO2 as a secondary ligand were prepared and characterized by elemental analysis (C.H.N), UV., FT-IR, magnetic susceptibility, μeff (B.M) as well as the conductivity measurements (Λm ). In the complexes, the 5-chlorosalicylic acid is bidentate in all complexes coordinating through –OH- and –COO- groups; also L-Valine behaves as a bidentate ligand in all complexes through –NH2 and –COO- groups. These five mixed ligand complexes formulated as Na3[M(CSA)2(L-Val)]. The proposed molecular structure for all complexes is octahedral geometries. The synthesis complexes were tested in vitro for against four bacteria