Heat treatment by solid solution method in the ?+? phase region was used at 970°C for Ti-5Al-2.5Fe alloy. The specimens cooled under different cooling media [water quenched (WQ), air cooled (AC) and furnace cooled (FC)], and subsequently aged at 550°C for 4 hours. Five specimens from each treatment were immersed in simulated body fluid SBF for a period of time (3 months). The dependence of corrosion rate on compositional variation in the phases resulted from various type of cooling rates are discussed based on immersion tests. The EDXA results show the precipitation of phosphate and calcium compounds on the alloy after 3 months of immersion in blood plasma solution forming a bone-like apatite, which enhanced the alloy biocompatibility ma

The inverse problem is important method in the design of electrostatic lenses which is used in this work, with new technique by suggesting an axial electrostatic potential distribution using polynomial functions of the third order. The paraxial-ray equation is solved to obtain the trajectory of particles that satisfy the suggested potential function.In this work design of immersion electrostatic lens operated under zero magnification condition. The electrode shape of sthe electrostatic lens was the dermined from the solution of laplace equation and plotted in two deimensions . The results showed low values of spherical and chromatic aberrations , which are considered as good criteria for good desigh.

 Theoretical study computerized has been carried out in electron optics field, to design electrostatic immersion lens , the inverse problem is important method in the design of electrostatic lenses by suggesting an axial electrostatic potential distribution using polynomial function. The paraxial –ray equation is solved to obtain the trajectory particles that satisfy the suggested potential function. In this research, designed immersed lens length L = 10mm operated under zero condition, as it was obtained the electrode shape of this lens solutions using the Laplace equation The results of the search showed low values of spherical and chromatic aberrations, which gives a good indication of the design of the lens.   It was

Polymer electrolytes were prepared using the solution cast technology. Under some conditions, the electrolyte content of polymers was analyzed in constant percent of PVA/PVP (50:50), ethylene carbonate (EC), and propylene carbonate (PC) (1:1) with different proportions of potassium iodide (KI) (10, 20, 30, 40, 50 wt%) and iodine (I₂) = 10 wt% of salt. Fourier Transmission Infrared (FTIR) studies confirmed the complex formation of polymer blends. Electrical conductivity was calculated with an impedance analyzer in the frequency range 50 Hz–1MHz and in the temperature range 293–343 K. The highest electrical conductivity value of 5.3 × 10^-3 (S/cm) was observed for electrolytes with 50 wt% KI concentration at room

In this paper, a polymer-based composite material was prepared by hand Lay-up method consisting of epoxy resin as a base material filled with by magnesium oxide powder once and silicon dioxide powder again and with different weight ratios (3%, 6%, 9%, 12%). The three-point bending test was performed in normal conditions and after immersion in sulfuric acid. The results showed that the bending value decreased with the increase of the weighted ratio of the filled nano powder (MgO, SiO₂) .The Bending of samples filled with by SiO₂ was found to be less than the bending of samples filled with by particles (MgO), the bending of the SiO₂ sample (0.32mm) at the weighted ratio (3%) and for the MgO (0.18mm) sample

In this research Epoxy resin was reinforced by nano alumina (AL2O3) particles in grain size(25-30 nm) with two weight ratios (2,4)% then compared with pure Epoxy. Four mechanical tests were performed on these materials include Hardness, flexural, impact & compression strengths before and after immersion in tap water and chemical solutions (CH3COOH) acid, (KOH) base at (0.5N) ,The diffusivity coefficients of all prepared samples were calculate after immersion in water and chemical solutions mentioned above , the results were showed that the Flexural, Impact & Hardness increase after addition the ceramic particles (AL2O3) while the immersion process results showed illustrated different values from sample to other.

The present work aimed to study the SiO2μPs, and NPs effect on the biodegradability of St/PVA blends. The samples were prepared by casting method as PVA, St/PVA blends with different concentrations (30, 40, 50, and 60 %). FTIR test was carried out for the samples preparation. The results proved some changes which might be related to changing in crystallinity of St/PVA matrix as well as physical incorporation of SiO2 μPs, and NPs addition. The enzymatic test and water uptake results proved that increase in weight loss with increases of starch ratio. The lowest weight loss was PVA; the highest weight loss is 60% St/PVA whereas the lowest weight loss is 30%St/PVA for blends involved. SiO2μPs (753.7 nm), and NPs (263.1 nm) were added at d

The present work studies the mechanical properties of SiO2 μPs, and NPs in St/PVA blends. The samples were prepared by casting method as PVA, St/PVA blends at different concentrations (30, 40, 50, and 60 %). DSC and TGA tests were carried out to the samples evolved. The result showed a single glass transition temperature (Tg) for all St /PVA blends that was attributed to the good miscibility of the blends involved. It was found that (Tg) decrease with starch ratio increase. It was seen that (PVA) of (Tg=105 oC); The glass transition temperature which was decrease with starch ratio that was attributed to glass transition relaxation process due to micro-Brownian motion of the main chain back bond. The endothermic peak at 200 oC was attrib