Ceramic body as a refractory was prepared by using shamoot, which is prepared by firing  kaolin Duekhla at 1450 ºC at 2hr ,Flint clay ,Asbestos fiber(Anthophylite type)and Sodium silicts,Phosphoric acid solution as a binder . After miling, siving ,and mixing ,samples were formed, followed that drying, firing at different temperature.     Phyical ,thermal and mechanical  properties were measured .The conclusion behind the results that the refractory prepared from; 37.5% shamoote,25% Asbestos ,37.5% Flint clay and Phosforic acid solution fired at 1300 ºC  gave a refractory material having  melting temperature ;1490 ºC, thermal shock resistance 7 cycle, thermal conductivity 2.1w/m2.K, apperan

Biomimatic basic calcium phosphate ,known as Hydroxy apatite(HA), was
synthesised using calcium acetate and disodium phosphate dilute hot (boiling) solution of
both salts were added slowly to each other. A colloidal suspension formed was aged for few
days, then boiled for one hour to induced setting and coagulation of preapatite, and left to cool
until they reached room temperature.
The precipitate was filtered and washed with distilled water, then ethanol and dried.
The dried sample was calcined at 1100
o
C.The obtained solid lumps were then crushed
reground fine powder and analyzed for calcium to phosphorous ratio. X-ray analysis was
carried out to examine the solid sample. Chemical analysis for phos

Hemorrhoids are one of the most common surgical conditions. The hemorrhoid may cause symptoms that are: bleeding, pain, prolapse, itching, spoilage of feces, and psychologic discomfort. There are many methods for treatment of hemorrhoid like, medical therapy, rubber band ligation, electerocoagulation, stapled hemorrhoidpexy, photocoagulation, sclerothereapy, doppler guided artery ligation, Cryosurgery, and surgery. All methods for treatment of hemorrhoids have advantages, disadvantages, and limitations. Conventional haemorrhoidectomy was the traditional operation for the treatment of hemorrhoids. But recently other modalities of treatment had been used as an alternative operations including CO2 laser haemorrhoidectomy. This work aims to

The research work covers a study of the possibility of producing porous ceramic bodies
as a thermal insulators by adding fired Dechla kaolinite (grog)to the same non burned
kaolinite.
Different weight percentage ranged between (0,15,25,35and40)from grog and sawdust
passed through mesh 50 to Deuchla-clay kaolinit.Cylindrical shape samples (30mm diameter
and 30mm height) were prepared by the semi-dry methed,moulding pressure was 50 N/mm
2
.
After drying at 110
o
c,the samples were burnet in the furnace at temperatures
900,950,1000,1050,and 1100
o
c. The sawdust burnt out and leaves air spaces which contribute
to the high thermal insulation value.
The fired samples were investigated to de

The physical, mechanical, electrical and thermal properties containing (Viscosity, curing, adhesion force, Tensile strength, Lap shear strength, Resistively, Electrical conductivity and flammability) of adhesive material that prepared from Nitrocellulose reinforced with graphite particles and aluminum streat. A comparison is made between the properties of adhesive material with varying percentage of graphite powder (0%, 25%, 30%, 35%, 40%) to find out the effect of reinforcement on the adhesive material. The ability of property an electrical was studied through the measurement of conductivity a function of temperature varying. The results of comparison have clearly shown that the increasing of conten

Polyvinyl alcohol, (PVA) was prepared using polyvinyl acetate emulsion (manufactured by Al-Jihad factory,
That-Al-Sawary Company) as a local raw material. In this investigation, polyvinyl acetate emulsion was converted to
solid form by coagulation the polymer from its emulsion using sodium sulphate salt as coagulant aid, then alcoholyzed
the solid polyvinyl acetate in methanol using sodium hydroxide as catalyst, polyvinyl alcohol produced by this method is
a dry, white to yellow powder.
Three affecting variables on the degree of hydrolysis of PVA were studied, these variable are Catalyst to
polymer weight ratio in the range of 0.01 – 0.06, reaction time in the range of 20 – 90 min, and reaction temperature in
the

   This work was carried out to investigate the shrinkage properties of insulator ceramic body, and the effect of changing the ratio of concentration of electrolyte solution on these properties. The electrical insulator body was prepared by using Iraqi local materials. These are :- kaolin Duakhla, Arudhuma Sand glass, and potash feldspar with weight percentage (45%, 25%,and 30%) respectively. The processes of milling, classification, mixing, forming and firing, through the process of mixing electrolyte solution and mineralizer were added at different concentrations for electrolyte solution, (1%, 0.7%, 0.5%, 0.2%, and 0.1%).  The electrolyte solution was prepared by mixing sodium carbonate and sodium silicate by (2:1) ratio

In this paper, silicon carbonitried thin films were prepared by the method of photolysis of the silane (SiH4) and ethylene (C2H4) gases, with and without ammonia gas (NH3), which is represented by the ratio between the (PNH3) and (PSiH4 + PC2H4 + PNH3), (which assign by the letter X), X has the values (0, 0.13, 0.33). This method carried out by using TEA-CO2 laser, on glass substrate at (375 oC), deposition rate (0.416-0.833) nm/pulse thin film thickness of (500-1000) nm. The optical properties of the films were studied by using Absorbance and Transmittance spectrums in wavelength range of (400-1100) nm, the results showed that the electronic transitions is indirect and the energy gap for the SiCN films increase with increasing of nitrog

In this paper waste natural material (date seed) and polymer particles(UF) were used for investigation of  removal dye of the potassium permanganate. Also study effect some variables such as pH, dye concentration and adsorbent concentration on dye removal. 15 experimental runs were done using  the itemized conditions designed established on the Box-Wilson design employed to optimize dye removal. The optimum conditions for the dye removal were found: (pH) 12, (dye con.) 2.38 ppm, (adsorbant con.) 0.0816 gm for date seed with 95.22% removal and for UF (pH) 12, (dye con.) 18 ppm, (adsorbant con.) 0.2235 gm with 91.43%. The value of R-square was 85.47%  for Date seed  and (88.77%) for UF.

Abstract: Objectives: To investigate the effect of temperature elevation on the bonding strength of resin cement to the zirconia ceramic using fractional CO2 laser. Background: Fractional CO2 laser is an effective surface treatment of zirconia ceramic, as it increases the bonding strength of zirconia to resin cement. Methods: Thirty sintered zirconia discs (10 mm diameter, 2 mm thickness) were prepared and divided to three groups (N=10) and five diffident pulse durations were used in each group (0.1, 0.5, 1, 5 and 10 ms). Group A was treated with 10 W power setting, group B with 20 W and group C with 30 W. During laser irradiation, temperature elevation measurement was recorded for each specimen. Luting cement was bonded to the treated z