The Ge0.4Te0.6 alloy has been prepared. Thin films of Ge0.4Te0.6 has been prepared via a thermal evaporation method with 4000A thickness, and rate of deposition (4.2) A/sec at pressure 2x10-6 Torr. The A.C electrical conductivity of a-Ge0.4Te0.6 thin films has been studied as a function of frequency for annealing temperature within the range (423-623) K, the deduced exponent s values, was found to decrease with increasing of annealing temperature through the frequency of the range (102-106) Hz. It was found that, the correlated barrier hopping (CBH) is the dominant conduction mechanism. Values of dielectric constant ε1 and dielectric loss ε2 were found to decrease with frequency and increase with temperature. The activation energies have

 In the present work polymer electrolytes were formulated using the solvent casting technique. Under special conditions, the electrolyte content was of fixed ratio of polyvinylpyrolidone (PVP): polyacrylonitrile (PAN) (25:75), ethylene carbonate (EC) and propylene carbonate (PC) (1:1) with 10% of potassium iodide (KI) and iodine I₂ = 10% by weight of KI. The conductivity was increased with the addition of ZnO nanoparticles. It is also increased with the temperature increase within the range (293 to 343 K). The conductivity reaches maximum value of about (0.0296 S.cm^-1) with (0.25 g) ZnO. The results of FTIR for blend electrolytes indicated a significant degree of interaction between the polymer blend (PVP and PAN)

The relative dielectric permittivity (dielectric constant) values for various materials are measured on site. The calculated values that are derived from measuring the ratio of the electrical capacitance of a cell when the sample of the material is placed. Parallel plate technique that consists of two parallel circular metallic plates is used. The instrument made up of aluminum which acts as electrodes and stuffed inside the PVC cylinder. Then the thin sheet of material (models) sandwiched between the two plates. Calculation of dielectric constant (εr) through this new technique gives a new velocity value of electromagnetic wave that propagates underground. These measured velocity values will utilize in Ground Penetration Radar (GPR) da

This search study the effect of particle size of graphite on the mechanical and thermal properties of epoxy composites, where graphite adopted with particle sizes (45,53,75) ?m, respectively, and the percentages by weight (0,1,3,5,7,9)% for each size of this three particle sizes.Mechanical properties represented by the bending (three-point bending) and through which the conclusion is bending stress and modulus of elasticity, thermal properties were either through thermal conductivity tests.The results showed that the ratio(1%) is the maximum value of bending stress at the three particle size and the (45 ?m) is the maximum.Thermal conductivity result show is the maximum value at ratio (1%) of particle size(53 ?m)

PMMA films of different thickness (0.006, 0.0105, 0.0206, 0.0385 and 0.056cm) were synthesized by casting process. The temperature and frequency dependence of dielectric constant and AC electrical conductivity measurements at various frequencies (10kHz-10MHz) and temperatures (293-373K) were carried out. Few anomalies in dielectric studies were observed near 313 and 373 K respectively. These points were related to glass transitions temperature. The variation of activation energy and conduction behavior was studied .From the AC conduction studies, it is confirmed that the mechanism responsible for the conduction process is hopping of carriers. The variations of the dielectric constant and loss as function of frequency at different tempera

Manganese dioxide rotating cylinder electrode prepared by anodic deposition on a graphite substrate using MnSO4 solution in the presence of 0.918 M of H2SO4. The influence of different operational parameters (MnSO4 concentration, current density, time, and rotation speed) on the structure, and morphology of MnO2 deposit film was examined widely. The structure and crystal size determined by X-ray diffraction (XRD), the morphology examined by scanning electron microscopy (SEM) and atomic force microscopy (AFM) techniques. The γ-MnO2 obtained as the main product of the deposition process. It found that the four parameters have a significant influence on the structure, morphology, and roughness of the prepared MnO2 deposit. The crystal size in

PVC-LiF composites films with different lithium fluoride (LiF) concentrations (0, 30, 50, and 70 weight %) were prepared by using the casting method. This research deals with the investigation of dielectric properties for PVC-LiF composite films as a function of frequency and temperature in the ranges of 100 to 10⁷ Hz and 293 - 370 K, respectively. The A.C activation energy values estimated from Arrhenius equation were 0.03820, 0.3174, 0.2009, and 0.1845 eV for the different PVC-LiF films with different LiF concentrations, respectively.  It was found that the activation energy decreases by increasing LiF concentration and frequency. The exponent (s) showed a progressive increase with LiF for PVC-LiF films, while it showed

The effects of reinforcing polymers with glass and graphite particles on enhancing their flexural properties are investigated.   Five composites were fabricated using the same polymer matrix material with different volume fractions of reinforcement particles. They comprise glass particles and graphite particles each  having volume fractions of 20% and 30% as well as a hybrid composite having 10% glass and 10% graphite. Three-point bending tests using a Universal Testing Machine were carried out on specimens of the above mentioned composites, as well as specimens of the polymer matrix material to determine their flexural properties. The experimental test results indicate that the flexural stiffness of all the composites wer

In this research prepared Epoxy – Talc powder composites with weight ratio of Talc powder (0,5,10,15,20,25)% . The value of thermal conductivity increase with increasing ratio of talc powder and water absorption increase with increasing ratio of talc powder because the structure from magnesium silicate hydroxide and hydrophilic nature .Ethanol absorption decrease with increasing percentage talc powder compared with epoxy pure

Graphite coated electrodes (GCE) based on molecularly imprinted polymers were fabricated for the selective potentiometric determination of Glibenclamide (Glb). The molecularly imprinted (MIP) and nonimprinted (NIP) polymers were synthesized by radical bulk polymerization using (Glb.) as a template, acrylic acid (AA) and acrylamide (AAm) as monomers, ethylene glycol dimethacrylate (EGDMA) as a cross-linker and benzoyl peroxide (BPO) as an initiator. The imprinted membranes and the non-imprinted membranes were prepared using dioctyl phthalate (DOP) and Dibutylphthalate (DBP) as plasticizers in PVC matrix. The membranes were coated on graphite electrodes. The MIP electrodes using (AA) and (AAm) showed a near nernstian response with slopes o