Study the Performance of Nanozeolite NaA on CO2 Gas Uptake
...Show More Authors

The adsorption isotherms and kinetic uptakes of CO2 were measured. Adsorption isotherms were measured at two temperatures 309 K and 333 K and over a pressure range of 1 to 7 bar. Experimental data of CO2 adsorption isotherms were modeled using Langmuir, Freundlich and Temkin. Based on coefficient of correlation it was found that Langmuir isotherm model was well suited with the experimental data of CO2 adsorption isotherms.  In addition, Adsorption kinetic of CO2 mixture with N2 containing 10 % by volume CO2 and 90 % by volume N2 were determined in a temperature 36 °C and under the atmospheric pressure .When the flow rate was increased from 0.5 l/min to 2 l/min the time required for complete column saturation decreased. Also the effect of bed length on breakthrough curves was studied. The adsorption capacity increases by bed length increasing for adsorption of carbon dioxide.

View Publication Preview PDF
Quick Preview PDF
Publication Date
Wed May 31 2017
Journal Name
Journal Of Engineering
Synthesis of Nanozeolite NaA from Pure Source Material Using Sol Gel Method
...Show More Authors

In this work, the nano particles of Na-A zeolite were synthesized by sol –gel method. The samples were characterized by X-ray diffraction (XRD), X-ray  luorescence (XRF), Surface  area and pore volume, Atomic Force Microscope (AFM) and Fourier Transform Infrared Spectroscopy (FTIR). Results show that the nano A zeolite is with average crystal size is 74.77 nm., Si/Al ratio 1.03, BET surface area was 581.211m2/g and the pore volume for NaA was found equal to 0.355cm3/g.
 
 
 

View Publication Preview PDF
Publication Date
Sun Jun 12 2011
Journal Name
Baghdad Science Journal
Study the effective of annealing on the structural and sensitivity properties for SnO2 thin films to CO2 Gas
...Show More Authors

In this research thin films from SnO2 semiconductor have been prepared by using chemical pyrolysis spray method from solution SnCl2.2H2O at 0.125M concentration on glass at substrate temperature (723K ).Annealing was preformed for prepared thin film at (823K) temperature. The structural and sensing properties of SnO2 thin films for CO2 gas was studied before and after annealing ,as well as we studied the effect temperature annealing on grain size for prepared thin films .

View Publication Preview PDF
Crossref
Publication Date
Tue Oct 08 2002
Journal Name
Iraqi Journal Of Laser
Effect of Gas Mixture on the Output Characteristics of a CW CO2 Laser
...Show More Authors

In this work, the effect of partial amounts of gases in gas mixture of a CW CO2 laser on the output power was investigated. Also their effect on the condition determining the glow-discharge self-sustaining required for pumping the active medium was studied. Two fit relations were derived to predict the output laser power and the electric field to unit pressure ratio as functions to the partial amounts of gases. Results presented in this work could be used fruitfully to determine some of the optimum operational conditions of glow-discharge low-power CW CO2 lasers.

View Publication Preview PDF
Publication Date
Tue Jan 01 2019
Journal Name
Energy Procedia
Studying the effect of adding buffer gases to CO2 gas on the electron transport parameter
...Show More Authors

View Publication
Scopus (3)
Crossref (2)
Scopus Clarivate Crossref
Publication Date
Tue Jan 01 2019
Journal Name
Desalination And Water Treatment
Effect of synthesis parameters on the formation 4A zeolite crystals: characterization analysis and heavy metals uptake performance study for water treatment
...Show More Authors

View Publication
Scopus (41)
Crossref (30)
Scopus Clarivate Crossref
Publication Date
Mon Oct 01 2018
Journal Name
Iraqi Journal Of Physics
Synthesis of gold nanoparticles by laser ablation on porous silicon for sensing CO2 gas
...Show More Authors

In this research, porous silicon (PS) prepared by anodization etching on surface of single crystalline p-type Si wafer, then Gold nanoparticle (AuNPs) prepared by pulsed laser ablation in liquid. NPs deposited on PS layer by drop casting. The morphology of PS, AuNPs and AuNPs/PS samples were examined by AFM. The crystallization of this sample was characterized by X-ray diffraction (XRD). The electrical properties and sensitivity to CO2 gas were investigated to Al/AuNPs/PS/c-Si/Al, we found that AuNPs plays crucial role to enhance this properties.

View Publication Preview PDF
Crossref (1)
Crossref
Publication Date
Sun Nov 19 2017
Journal Name
Iraqi Journal Of Laser
Sulfur Hexafluoride (SF6) Trace Gas Sensing using Modulated CO2 Laser Beam
...Show More Authors

Photonic Crystal Fiber Interferometers (PCFIs) are widely used for sensing applications. This work presents the fabrication and the characterization of a relative humidity sensor based on a polymer-coated photonic crystal fiber that operates in a Mach- Zehnder Interferometer (MZI) transmission mode. The fabrication of the sensor involved splicing a short (1 cm) length of Photonic Crystal Fiber (PCF) between two single-mode fibers (SMF). It was then coated with a layer of agarose solution. Experimental results showed that a high humidity sensitivity of 29.37 pm/%RH was achieved within a measurement range of 27–95%RH. The sensor also showed good repeatability, small size, measurement accuracy and wide humidity range. The RH sensitivity o

... Show More
View Publication Preview PDF
Publication Date
Sun Dec 01 2002
Journal Name
Iraqi Journal Of Physics
Preparation of thin films of SiCN from gas-phase reaction induced by TEA-CO2 laser and study of their optical properties
...Show More Authors

In this paper, silicon carbonitried thin films were prepared by the method of photolysis of the silane (SiH4) and ethylene (C2H4) gases, with and without ammonia gas (NH3), which is represented by the ratio between the (PNH3) and (PSiH4 + PC2H4 + PNH3), (which assign by the letter X), X has the values (0, 0.13, 0.33). This method carried out by using TEA-CO2 laser, on glass substrate at (375 oC), deposition rate (0.416-0.833) nm/pulse thin film thickness of (500-1000) nm. The optical properties of the films were studied by using Absorbance and Transmittance spectrums in wavelength range of (400-1100) nm, the results showed that the electronic transitions is indirect and the energy gap for the SiCN films increase with increasing of nitrog

... Show More
View Publication Preview PDF
Publication Date
Fri Feb 08 2019
Journal Name
Iraqi Journal Of Laser
Evaluation the Effects of CO2 Laser on Soft and Hard Tissues (in vitro study)
...Show More Authors

CO2 laser (10.6 μm) is the most often used laser in the oral surgery due to its high absorption by water of the oral tissues. Several benefits of the use of CO2 laser have been reported for oral surgical procedures. This study aims to evaluate the effect of CO2 laser on soft and hard oral tissues (in vitro study). This study was done on fresh tissues from sheep’s head. CO2Surgical Laser with different operation modes was used; 0.2 mm spot size using different laser parameters on the tongue, and bone making holes, incisions and cutting. The depths and widths of holes and incisions were measured using endodontic file under magnification. The speed of incisions was calculated and the required time for cutting was measured using sport clo

... Show More
View Publication Preview PDF
Publication Date
Thu Aug 01 2024
Journal Name
Fuel
Experimental influence assessments of water drive and gas breakthrough through the CO2-assisted gravity drainage process in reservoirs with strong aquifers
...Show More Authors

Mature oil reservoirs surrounded with strong edge and bottom water drive aquifers experience pressure depletion and water coning/cresting. This laboratory research investigated the effects of bottom water drive and gas breakthrough on immiscible CO2-Assisted Gravity Drainage (CO2-AGD), focusing on substantial bottom water drive. The CO2-AGD method vertically separates the injected CO2 to formulate a gas cap and Oil. Visual experimental evaluation of CO2-AGD process performance was performed using a Hele-Shaw model. Water-wet sand was used for the experiments. The gas used for injection was pure CO2, and the “oleic” phase was n-decane with a negative spreading coefficient. The aqueous phase was deionized water. To evaluate the feasibilit

... Show More
View Publication
Scopus (1)
Crossref (2)
Scopus Clarivate Crossref