Gamma - irradiation effect on polymethylmethacrylate (PMMA) samples has been studied using Positron Annihilation Lifetime (PAL) method. The orthopositronium (o-Ps) lifetime τ₃, hence the o-ps parameters, the volume hole size (V_h) and the free volume fraction (Ꞙ_h) in the irradiated samples were measured as a function of gamma-irradiation dose up to 28.05 kGy. It has been shown that τ ₃, V_h, and Ꞙ_h, are increasing in general with increasing gamma-dose, to reach a maximum percentage increment of 22.42% in τ₃, 60% in V_h and 29.5% in Ꞙ_h, at. 2.55 kGy, whereas τ₂ reaches maximum increment of 119. 7% at 7.65 kGy. The results s

The research is concerned about studying the absorption spectrum of the solution coumarin dye C47. The chloroform solvent was used with C47 dye in three different concentrations 10-4, 10-5 and 10-6 M. The laser dye solution was prepared by dissolving the required amount of dye in chloroform alcohol, while studying absorption spectrum before and after irradiation with gamma ray by cobalt-60 source 60Co at exposure time, which are 0, 4, 6 and 18 hours with different absorbed doses 0, 136, 204 and 612 Gy. The results show that red shift in the absorption spectrum was increased by increasing the concentration of laser dye solutions , while the increase of gamma dose led to increase the red shift after irradiation, as the exposure period and irr

Positron annihilation lifetime (PAL) technique has been employed to
study the microstructural changes of polyurethane (PU), EUXIT 101
and epoxy risen (EP), EUXIT 60 by Gamma-ray irradiation with the
dose range (95.76 - 957.6) kGy. The size of the free volume hole and
their fraction in PU and EP were determined from ortho-positronium
lifetime component and its intensity in the measured lifetime spectra.
The results show that the irradiation causes significant changes in the
free volume hole size (V_h) and the fractional free volume (F_h), and
thereby the microstructure of PU and EP. The results indicate that
the γ-dose increases the crystallinity in the amorphous regions of PU
and increas

Abstract: In the current research the absorption and fluorescence spectrum of Coumarin (334) and Rhodamine (590) in ethanol solvent at different concentration (10-3, 10-4, 10-5) M had been studied. The absorption intensity of these dyes increases as the Concentration increase in addition to that the spectrum was shifted towards the longer wavelength (red shift). The energy transfer process has been investigated after achievement this condition. The fluorescence peak intensity of donor molecule was decrease and its bandwidth will increases on the contrary of the acceptor molecule its intensity increase gradually and its bandwidth decreases as the acceptor concentration increase.

In the current research the absorption and fluorescence spectrum
of Coumarin (334) and Rhodamine (590) in ethanol solvent at
different concentration (10-3, 10-4, 10-5) M had been studied. The
absorption intensity of these dyes increases as the Concentration
increase in addition to that the spectrum was shifted towards the
longer wavelength (red shift). The energy transfer process has been
investigated after achievement this condition. The fluorescence peak
intensity of donor molecule was decrease and its bandwidth will
increases on the contrary of the acceptor molecule its intensity
increase gradually and its bandwidth decreases as the acceptor
concentration increase.