Interfacial Bond Strength and Morphology of Sound and Caries-affected Dentin Surfaces Bonded to Two Resin-modified Glass Ionomer Cements
...Show More Authors
SUMMARY<sec> <title>Objective

To evaluate the shear bond strength and interfacial morphology of sound and caries-affected dentin (CAD) bonded to two resin-modified glass ionomer cements (RMGICs) after 24 hours and two months of storage in simulated body fluid at 37°C.

Methods and Materials

Sixty-four permanent human mandibular first molars (32 sound and 32 with occlusal caries, following the International Caries Detection and Assessment System) were selected. Each prepared substrate (sound and CAD) was conditioned (10% polyacrylic acid) and bonded to Activa BioACTIVE Restorative (Activa) and Fuji II LC (F2LC) as per the manufacturers’ instructions. Shear bond strength (SBS) was performed after 24 hours and two months of storage. The interfacial surfaces were examined using a digital microscope and scanning electron microscope (SEM). Three-way ANOVA, Bonferroni post-hoc tests (α=0.05), and independent T-tests were used for multifactorial analysis.

Results

Activa exhibited reduced bond strength values to sound and CAD in comparison to F2LC after two time periods (p=0.01). There is a pronounced enhancement in SBS of F2LC when bonded to CAD (p=0.01) after storage, with no statistically significant effect on sound dentin (p=0.309). Activa showed stable SBS to sound and CAD immediately and post-aging (p&gt;0.05). However, the evidence of mineral-like deposits under an SEM attached to the aged, debonded dentin surfaces, thereby obliterating the exposed dentinal tubules, might support the tissue repair potential of Activa.

Conclusions

The SBS of Activa was lower than F2LC when bonded to sound and CAD, but the bonding stability and sealing ability is advantageous in minimally invasive therapy, suggesting use with a resin composite coverage when used in stress-bearing areas.

View Publication
Publication Date
Sat Apr 05 2025
Journal Name
Journal Of Baghdad College Of Dentistry
Shear bond strength of different lingual buttons bonded to wet and dry enamel surfaces with resin modified glass ionomer cement (in vitro comparative study)
...Show More Authors

Background: This study was aimed to investigate the effect of three lingual button (Nickel free / rectangular base, Nickel free / round base and Composite) and bonding environment, wet and dry enamel surface, on: the shear bond strength (SBS) of light and self-cured Resin Modified Glass Ionomer Cements, and the debonding failure sites. Materials and method: One hundred twenty no-carious, free of cracks maxillary first premolar teeth were selected. Three types of orthodontic lingual buttons were used in this study: Nickel free / rectangular base, Nickel free / round base and Composite buttons. The teeth were divided into two groups of sixty teeth each. One group was used for testing the chemically cured GC Fuji Ortho Resin modified Glass Io

... Show More
View Publication Preview PDF
Publication Date
Wed May 01 2024
Journal Name
Journal Of International Society Of Preventive And Community Dentistry
Effect of Incorporating Chitosan to Resin Modified Glass Ionomer Cement on Shear Bond Strength to Dentin (An In vitro Comparative Study)
...Show More Authors
A<sc>bstract</sc> <sec> <title>Aim:

Resin-modified glass ionomer cement tends to shrink due to polymerization of the resin component. Additionally, they are more prone to syneresis and imbibition during the setting process. This in vitro study evaluates the impact of chitosan, a biopolymer that is, both biomaterial and biocompatible, on the strength of dentin bonding and compares it with ACTIVA Bio-ACTIVE Restorative. The present study was aimed to assess the impact of including chitosan into Fuji II on the shear bond strength between. the restoration material and tooth dentin,

... Show More
View Publication
Scopus Clarivate Crossref
Publication Date
Tue May 07 2024
Journal Name
Heliyon
Micro-shear bond strength of a novel resin-modified glass ionomer luting cement (eRMGIC) functionalized with organophosphorus monomer to different dental substrates
...Show More Authors

Objectives: This study aims to assess and compare the micro-shear bond strength (μSBS) of a novel resin-modified glass-ionomer luting cement functionalized with a methacrylate co-monomer containing a phosphoric acid group, 30 wt% 2-(methacryloxy) ethyl phosphate (2-MEP), with different substrates (dentin, enamel, zirconia, and base metal alloy). This assessment is conducted in comparison with conventional resin-modified glass ionomer cement and self-adhesive resin cement. Materials and methods: In this in vitro study, ninety-six specimens were prepared and categorized into four groups: enamel (A), dentin (B), zirconia (C), and base metal alloys (D). Enamel (E) and dentin (D) specimens were obtained from 30 human maxillary first premolars e

... Show More
Preview PDF
Publication Date
Sat Sep 28 2024
Journal Name
Journal Of International Dental And Medical Research
Effect of Air–Particle Abrasion of Dentin Surface on Shear Bond Strength of Lithium Disilicate to Dentin Using Three Different Cements
...Show More Authors

This study aims to evaluate the influence of the air abrasion of dentin on the shear bond strength of lithium disilicate using three different types of luting cements. Sixty cylindrical specimens were milled from lithium disilicate CAD/CAM blocks (IPSe.max CAD). Sixty sound human maxillary premolar teeth were decoronated to the level of peripheral dentin, then randomly divided into three groups according to the type of luting cement used for the cementation of the lithium disilicate specimens (n = 20); Group A: Glass ionomer cement (Riva Self- Cure); Group B: Adhesive resin cement (Rely X Ultimate); Group C: Self-adhesive resin cement (Rely X U200). Each group was then further subdivided into two subgroups (n=10); Subgroups AI, BI, and CI,

... Show More
Preview PDF
Scopus
Publication Date
Tue Mar 01 2022
Journal Name
Journal Of Dentistry
In-vitro adhesive and interfacial analysis of a phosphorylated resin polyalkenoate cement bonded to dental hard tissues.
...Show More Authors

Objectives: To assess the performance of a novel resin-modified glass-ionomer cement (pRMGIC) bonded to various tooth tissues after two-time intervals. Methods: 192 sound human molars were randomly assigned to 3 groups (n = 64): sound enamel, demineralised enamel, sound dentine. Sixty-four teeth with natural carious lesions including caries-affected dentine (CAD) were selected. All substrates were prepared, conditioned and restored with pRMGIC (30% ethylene glycol methacrylate phosphate (EGMP, experimental), Fuji II LC (control), Fuji IX, and Filtek™ Supreme with Scotchbond ™ Universal Adhesive. Shear bond strength (SBS) was determined after 24 h and three months storage in SBF at 37C. The debonded surfaces were examined using stereomi

... Show More
View Publication
Scopus (7)
Crossref (8)
Scopus Clarivate Crossref
Publication Date
Fri Dec 15 2023
Journal Name
Journal Of Baghdad College Of Dentistry
Color stability of nano resin-modified glass Ionomer restorative cement after acidic and basic medications challenge
...Show More Authors

Background: Color stability of glass ionomers (GIs) could be affected by many factors such as pH and consumption of liquid medications like antibiotics. Most common antibiotics used during childhood are amoxicillin suspension (AM.S) and azithromycin suspension (AZ.S) which have acidic and basic pH respectively. Aim: to evaluate and compare the effect of AM.S and AZ.S on color stability of nano resin-modified GI. Methods: Thirty disc of nano resin-modified glass ionomer (2mm height x 4mm diameter) were divided into three groups (n=10 for each) and independently exposed to AM.S, AZ.S, and artificial saliva (A.S.). Color stability was evaluated in triplicate by VITA Easyshade® before and after three immersion protocols, repeated over a thr

... Show More
View Publication Preview PDF
Scopus (3)
Crossref (2)
Scopus Crossref
Publication Date
Tue Aug 11 2020
Journal Name
Bdj Open
An in vitro assessment of the physical properties of manually- mixed and encapsulated glass-ionomer cements
...Show More Authors
Abstract<sec> <title>Objectives

The last decade has seen a variety of modifications of glass-ionomer cements (GICs), such as inclusion of bioactive glass particles and dispensing systems. Hence, the aim was to systematically evaluate effect of mixing modes and presence of reactive glass additives on the physical properties of several GICs.

Materials and methods

The physical properties of eight commercial restorative GICs; Fuji IX GP Extra (C&H), KetacTM Fill Plus Applicap (C&H), Fuji II LC (C&H), Glass Carbomer Ce

... Show More
View Publication Preview PDF
Scopus (28)
Crossref (20)
Scopus Clarivate Crossref
Publication Date
Wed Sep 14 2016
Journal Name
Journal Of Baghdad College Of Dentistry
Comparison of Shear Bond Strength of Three Different Brackets Bonded on Zirconium Surfaces (In Vitro Study)
...Show More Authors

Background: With the increased in the demands of adult orthodontics, the challenge of direct bonding to non-enamel surface (zirconium) had been increased. The present study was carried out to compare the shear bond strength of three different brackets (stainless steel, sapphire and composite) bonded to zirconium surface and study the mode of bond failure. Materials and methods: The sample was comprised of 30 models (8mm *6mm*1.5mm) of full contour zirconium veneers. They were divided into three groups according to the brackets type; all samples were treated first by sandblast with aluminum oxide particle 50 µm then coated by z-prime plus primer. A central incisor bracket of each group was bonded to the prepared zirconium surface with lig

... Show More
View Publication Preview PDF
Crossref (2)
Crossref
Publication Date
Sat Apr 05 2025
Journal Name
Journal Of Baghdad College Of Dentistry
A comparative study to evaluate the shear bond strength of different resin sealers to dentin (An in vitro study)
...Show More Authors

Background: One of the major problems in endodontics is micro-leakage of root canal fillings which might contribute to the failure of endodontic treatment. To avoid this problem, a variety of sealers have been tested. The objective of this, in vitro, study was to evaluate the shear bond strength of four resin based sealers (AH plus, silver free AH26, RealSeal SE and Perma Evolution permanent root canal filling material) to dentin. Materials and Methods: Forty non-carious extracted lower premolars were used. The 2mm of the occlusal surfaces of teeth were sectioned, to expose the dentin surface. The exposed dentin surfaces of teeth were washed with 5ml of 2.5% NaOCl solution followed by 5ml of 17 % EDTA then rinsed by deionized water to remov

... Show More
View Publication Preview PDF
Publication Date
Sat Jun 15 2019
Journal Name
Journal Of Baghdad College Of Dentistry
Evaluation of The Microleakage of Polyacid Modified Composite Compared to Hybrid Composite and Resin Modified Glass Ionomer Cement in Primary and Permanent Teeth Restoration (An in vitro study)
...Show More Authors

Background: Dental caries is one of the most significant problems in world health care. Restoring carious primary teeth is one of the major treatment goals for Children, and the light activated resin restoration materials like composite, resin-modified glass ionomer and polyacid-modified which was introduced in dentistry in 1970, widely used in clinical dentistry but its application increased dramatically in recent years because of its biocompatibility, color matching, good adhesive properties of its resemblance in physical and mechanical aspects to tooth. The aim of this study: To evaluate the microleakage of Polyacid-Modified Composite resin Compared to Flowable Hybrid Composite and Resin-Modified Glass ionomer cement. Materials and me

... Show More
View Publication
Scopus (5)
Crossref (4)
Scopus Crossref